(BS1387,ASTM A53) Galvanized Steel Pipe

FOB Price

US $980.0010 - 40,000 ton

US $750.0040,001 - 999,999 ton

group name: TYT STEEL SCAFFOLDING

Min Order: 10 ton

brand name: TYTSTEEL

Nearest port for product export: TIANJIN XINGANG PORT, QINGDAO PORT, SHANGHAI PORT, NINGBO PORT

Delivery clauses under the trade mode: FOB, CFR, CIF, EXW, CIP, CPT, DDP, DDU

Acceptable payment methods: T/T, L/C, D/P D/A, MoneyGram, Credit Card, Westem Union, Escrow

update time: Tue, 22 Apr 2014 14:19:40 GMT

contact supplier

Paramtents

Standard BS, GB, ASTM
Standard BS 1387, BS 1139, BS 4568, BS EN 39, GB/T 3091-2001, ASTM A53-2007
Grade A53-A369, ST35-ST52, Q195-Q345
Grade A53(A,B), St37, St52, St42, Q235, Q345, Q195, Q215
Thickness 1.2 - 9 mm
Section Shape Round
Outer Diameter 20 - 273 mm
Secondary Or Not Non-secondary
Application Electrical,Fluid,construction scaffolding and conduct pipe
Technique ERW
Certification ISO9001:2000
Surface Treatment Galvanized
Alloy Or Not Non-alloy
Length 4 to 12meter
Zinc coating content 260-350 g/m2
Brand TYSTEEL
Life Over 10 years
Surface treatment Galvanized
Ends Screwed both ends and complete with one solid coupling(socket)
Usage Electrical,water transportation and conduct pipe

Packging & Delivery

Min Order10 ton

Briefing

Galvanized Steel Pipe
Standard: ASTM A53,BS1387,EN39,BS4568
Size:DN1/2"-8"
Thickness:1.2mm-7.5mm
Length:4-12meter

Detailed

ASTM A53 SCHEDULE 40 GRADE B
Outside Dia. Of Black /Galvanized tube Weight of Black /Galvanized tube

SIZE Minimum Maximum Wall Thickness Plain Ends Secrewed & Socketed Pieces
INCH NB(mm) INCHES mm Inches mm Inches mm lb./Ft. Kg./Mtr. lb./Ft. Kg./Mtr. per bundle Factory standard
1/2'' 15 0.809 20.9 0.856 21.7 0.109 2.77 0.85 1.27 0.85 1.27 120 217
3/4'' 20 1.020 26.3 1.070 27.1 0.113 2.87 1.13 1.69 1.13 1.69 84 169
1'' 25 1.280 33.0 1.330 33.8 0.133 3.38 1.68 2.50 1.68 2.50 60 127
11/4'' 32 1.630 41.8 1.680 42.6 0.140 3.56 2.27 3.39 2.28 3.40 42 91
11/2'' 40 1.870 47.9 1.920 48.7 0.145 3.68 2.72 4.05 2.73 4.06 36 91
2'' 50 2.350 59.7 2.400 60.9 0.154 3.91 3.65 5.44 3.68 5.46 26 37
21/2'' 65 2.850 72.3 2.900 73.7 0.203 5.16 5.79 8.63 5.82 8.67 18 37
3'' 80 3.460 88.0 3.530 89.8 0.216 5.49 7.58 11.29 7.62 11.35 14 37
31/2'' 90 3.960 100.6 4.040 102.6 0.226 5.74 9.11 13.57 9.20 13.71 12 19
4'' 100 4.450 113.2 4.540 115.4 0.237 6.02 10.79 16.07 10.89 16.20 10 19
5'' 125 5.510 139.9 5.620 142.7 0.258 6.55 14.62 21.77 14.81 22.10 7 19
6'' 150 6.560 166.6 6.690 169.98 0.280 7.11 18.97 28.26 19.18 28.60 7 19
1.TOLERANCE:
a)On Thickness: The minimum wall thickness at any point shall be not more than 12.5% under the nominalwall thickness specified.
b)On Diameter:For NPS 11/2" & under at any point shall not vary more than +/- 0.4mm. For NPS 2" & above shall not vary more than +/-1% from the standard specified.
c)On Weight: The weight of the pipe shall not vary by more than +/- 10% of the specified value.
2.ENDS:
a)11/2" and below size - End finish shall be at the option of manufacturer. Nominally square cut with theaxis of tube and free from excessive burrs.
b)2" and above size - Bevelled with ends bevelled to an angle of 30 degrees +5/-0 measured from a line perpendicular to the axis of the pipe with a root face of 1.6mm +/-0.8mm.
3.INTERNAL DEBEADING: From size 2" & above internal beads can be completely removed.
4.PROPERTIES:a) Chemical = (Maximum) C - 0.30%, Mn - 1.20%, S - 0.045% & P - 0.050%, Cu-0.40%, Ni-0.40%, Cr-0.40%,Mo-0.15%, V-0.08%, (Cu+Ni+Cr+Mo+V = 1.0% max)
b) Mechanical (Minimum) = UTS - 415 N/mm2, YS - 240 N/mm2 & %Elongation 19 to 25% .
5.BEND TEST (COLD): Applicable to tubes upto and including nominal size of 50mm.
a)When ordered for close coiling bend upto 180 degrees around a cylindrical mandrel, the Dia of which is 8 times the OD of pipe.
b)Bend upto 90 degree around a cylindrical mandrel, the dia of which is 12 times the OD of pipe .No cracks at any portion and no open in the weld.
6.FLATTENING TEST (COLD): Applicable to tubes greater than nominal size of 50mm weld located 0 / 90 degrees from the line of direction of force
a)During the 1st step, which is atest for ductility of the weld, no cracks or breaks in the inside or outside surfaces at the weld shall occur until the distance between the plates is less than two thirds of the specified diameter of the pipe.
b)During the 2nd step, no cracks or breaks on the inside or outside surfaces away from the weld, shall occur until the distance between the plates is less than one third of the specified outside diameter of the pipe but is less than five times the wall thickness of the pipe.
c) During the 3rd step, which is a test for soundness, flattening shall be continued until the test specimen breaks or the opposite walls of the pipe meet. Evidence of laminated or unsound material or of incomplete weld that is revealed by the flattening test shall be cause for rejection.
7.LEAK TIGHTNESS TEST:a) Online NDT (Eddy current ) b) Hydro test at a pressure of 700 PSI to 2500 PSI
8.BLACK VARNISH:Tubes are uniformly varnished externally over their full lengths.
9.ZINC COATING:Average 3000 Gm/M2, but one side should not be less than 260 Gm/M2. Free from bare spots,black spots,(GALVANIZING) rough,overcoating,peel off or any other surface defects.
10.THREADING:For 1/2" to 3/4" - 14 TPI, 1" to 2" - 11.5 TPI and 21/2" to 6" = 8 TPI.Check with standard ASTM ring and plug gauges.
11.MARKING:We can do online by stencilling as per this standard & as per customer needs at one meter interval.
12 PACKING:Hexagonal type.
13.MILL TEST CERTIFICATE:We can issue a MTC, certifying that the tubes supplied comply with this ASTM A 53 Standard.

ASTM A53 SCHEDULE 40 GRADE B
		Outside Dia. Of Black /Galvanized tube			Weight of Black /Galvanized tube

SIZE	Minimum	Maximum	Wall Thickness	Plain Ends		Secrewed & Socketed		Pieces
INCH	NB(mm)	INCHES	mm	Inches	mm	Inches	mm	lb./Ft.	Kg./Mtr.	lb./Ft.	Kg./Mtr.	per bundle	Factory standard
1/2''	15	0.809	20.9	0.856	21.7	0.109	2.77	0.85	1.27	0.85	1.27	120	217
3/4''	20	1.020	26.3	1.070	27.1	0.113	2.87	1.13	1.69	1.13	1.69	84	169
1''	25	1.280	33.0	1.330	33.8	0.133	3.38	1.68	2.50	1.68	2.50	60	127
11/4''	32	1.630	41.8	1.680	42.6	0.140	3.56	2.27	3.39	2.28	3.40	42	91
11/2''	40	1.870	47.9	1.920	48.7	0.145	3.68	2.72	4.05	2.73	4.06	36	91
2''	50	2.350	59.7	2.400	60.9	0.154	3.91	3.65	5.44	3.68	5.46	26	37
21/2''	65	2.850	72.3	2.900	73.7	0.203	5.16	5.79	8.63	5.82	8.67	18	37
3''	80	3.460	88.0	3.530	89.8	0.216	5.49	7.58	11.29	7.62	11.35	14	37
31/2''	90	3.960	100.6	4.040	102.6	0.226	5.74	9.11	13.57	9.20	13.71	12	19
4''	100	4.450	113.2	4.540	115.4	0.237	6.02	10.79	16.07	10.89	16.20	10	19
5''	125	5.510	139.9	5.620	142.7	0.258	6.55	14.62	21.77	14.81	22.10	7	19
6''	150	6.560	166.6	6.690	169.98	0.280	7.11	18.97	28.26	19.18	28.60	7	19
1.TOLERANCE:
a)On Thickness: The minimum wall thickness at any point shall be not more than 12.5% under the nominalwall thickness specified.
b)On Diameter:For NPS 11/2" & under at any point shall not vary more than +/- 0.4mm. For NPS 2" & above shall not vary more than +/-1% from the standard specified.
c)On Weight: The weight of the pipe shall not vary by more than +/- 10% of the specified value.
2.ENDS:
a)11/2" and below size - End finish shall be at the option of manufacturer. Nominally square cut with theaxis of tube and free from excessive burrs.
b)2" and above size - Bevelled with ends bevelled to an angle of 30 degrees +5/-0 measured from a line perpendicular to the axis of the pipe with a root face of 1.6mm +/-0.8mm.
3.INTERNAL DEBEADING: From size 2" & above internal beads can be completely removed.
4.PROPERTIES:a) Chemical = (Maximum) C - 0.30%, Mn - 1.20%, S - 0.045% & P - 0.050%, Cu-0.40%, Ni-0.40%, Cr-0.40%,Mo-0.15%, V-0.08%, (Cu+Ni+Cr+Mo+V = 1.0% max)
b) Mechanical (Minimum) = UTS - 415 N/mm2, YS - 240 N/mm2 & %Elongation 19 to 25% .
5.BEND TEST (COLD): Applicable to tubes upto and including nominal size of 50mm.
a)When ordered for close coiling bend upto 180 degrees around a cylindrical mandrel, the Dia of which is 8 times the OD of pipe.
b)Bend upto 90 degree around a cylindrical mandrel, the dia of which is 12 times the OD of pipe .No cracks at any portion and no open in the weld.
6.FLATTENING TEST (COLD): Applicable to tubes greater than nominal size of 50mm weld located 0 / 90 degrees from the line of direction of force
a)During the 1st step, which is atest for ductility of the weld, no cracks or breaks in the inside or outside surfaces at the weld shall occur until the distance between the plates is less than two thirds of the specified diameter of the pipe.
b)During the 2nd step, no cracks or breaks on the inside or outside surfaces away from the weld, shall occur until the distance between the plates is less than one third of the specified outside diameter of the pipe but is less than five times the wall thickness of the pipe.
c) During the 3rd step, which is a test for soundness, flattening shall be continued until the test specimen breaks or the opposite walls of the pipe meet. Evidence of laminated or unsound material or of incomplete weld that is revealed by the flattening test shall be cause for rejection.
7.LEAK TIGHTNESS TEST:a) Online NDT (Eddy current ) b) Hydro test at a pressure of 700 PSI to 2500 PSI
8.BLACK VARNISH:Tubes are uniformly varnished externally over their full lengths.
9.ZINC COATING:Average 3000 Gm/M2, but one side should not be less than 260 Gm/M2. Free from bare spots,black spots,(GALVANIZING) rough,overcoating,peel off or any other surface defects.
10.THREADING:For 1/2" to 3/4" - 14 TPI, 1" to 2" - 11.5 TPI and 21/2" to 6" = 8 TPI.Check with standard ASTM ring and plug gauges.
11.MARKING:We can do online by stencilling as per this standard & as per customer needs at one meter interval.
12 PACKING:Hexagonal type.
13.MILL TEST CERTIFICATE:We can issue a MTC, certifying that the tubes supplied comply with this ASTM A 53 Standard.

(BS1387,ASTM A53) Galvanized Steel Pipe